Osteosynthesis device

ABSTRACT

Intramedullary osteosynthesis device is capable of adopting a profiled H-shape in a closed introductory state in order to be easily implantable and an X-shape in an open implanted state for good fixation in the bone.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is the US national phase of PCT application PCT/FR2008/050453, filed 14 Mar. 2008, published 30 Oct. 2008 as WO2008/129214, and claiming the priority of French patent application 0702003 itself filed 20 Mar. 2007, whose entire disclosures are herewith incorporated by reference.

FIELD OF THE INVENTION

The invention relates to the technical field of orthopaedic implants, in particular for arthrodeses and osteosyntheses.

BACKGROUND OF THE INVENTION

It may be recalled that an osteosynthesis implant must serve to hold in place two (or more) parts of the same bone is fractured or cut by a surgical operation (osteotomy), for the time necessary for the consolidation of this bone (typically 3 months).

It may be recalled that an arthrodesis is the blocking of a joint by surgery to fuse two bones into a single one, using an osteosynthesis device.

It may be recalled that the purpose of any osteosynthesis and particularly in the case of an arthrodesis is to obtain very good primary and also secondary stability, in order to obtain the consolidation in the best possible conditions, that is, in a position selected by the surgeon, by minimizing the problems of post-operative pain and edemas, by shortening the consolidation time as much as possible.

To obtain this result, the stability of the osteosynthesis associated with the implant is critical. Furthermore, the implant must also provide and maintain a slight compression on the portions of bone to be fused together, thereby facilitating this consolidation.

Various technical solutions have been proposed to carry out an arthrodesis, in particular at the tips (foot, hand, wrist, ankle, etc.).

Mention can be made, for example of basic staples which do not provide a proper fixation during consolidation, and shape memory staples which serve to place the two bone portions to be consolidated under compression, thereby corresponding to the intended purpose.

However, to obtain satisfactory stability, it is necessary to place two, or even three staples, in different planes. This significantly increases their size, thereby limiting the applications, in particular on small bones (for example in the fingers or toes).

It is also common to use extramedullary or extra-osseous plates and screws, which also require a relatively large space and cannot be used on the terminal phalanges of the fingers (distal interphalangeal arthrodesis for example). Moreover, the medium-term stability of these systems is not always guaranteed (loosening of the mounting).

Certain types of screw can be used in intramedullary cases, but in this case, the approach path requires a pulpar approach, which may generate serious complications (sepsis, etc.) and discomfort for the patient.

Use can also be made of pins which have a smaller size. However, the stability obtained is not satisfactory (problems of migration) and it is generally necessary to remove them after consolidation. With such devices, moreover, the patient cannot immerse the finger or toe treated, because the pin generally projects outside the skin.

Intramedullary osteosynthesis systems are available for long bones (tibia, femur, humerus, etc.). For example, lockable centromedullary nails are known. Apart from the fact that the locking technique is difficult, it cannot be miniaturized for extremity surgery (hand and foot).

Shape memory intramedullary devices are also available for solving part of the problems with respect to the arthrodesis or the osteosynthesis of the small fragments: for example, the solutions described in French patent 2 846 545 or French patent 2 884 406 (US 2008/0177262).

French Patent 2 846 545 describes an H-shaped device which opens in the body into an X, thanks to the use of a shape is memory set around 37° C., each leg being implanted in a calibrated hole.

In practice, such a system does not allow proper introduction into the bone. This is because the preparation of 2 parallel holes in a phalange is extremely difficult due to the limited size and, above all, the parallel legs tend to open naturally during introduction and thereby exert an effect of distraction of the two fragments rather than compression.

Furthermore, the use of shape memory is very limiting due to the demands it makes on surgeons, in particular of temperature management: the implant must be fitted into the bone when cold before it warms and opens. This requires placing the implant in a support, storing it cold, and using all possible speed for implantation.

Finally, since the legs are straight, their shape memory tends to create a local support at their tips, which does not ensure satisfactory behavior and can damage the bone.

US 2008/0177262 teaches a system for easier introduction whether by the shape (eye) or by a support or a clamp that keeps the legs of the implant closed during introduction.

Nevertheless, these systems do not operate very dependably, because they do not define the optimal criteria allowing proper introduction into the bone and good anchorage: the anchoring zones always tend to open too early, thereby blocking introduction.

OBJECT OF THE INVENTION

It is the object of the invention to remedy all these drawbacks simply, reliably, effectively and efficiently.

The problem that the invention proposes to solve is to define the success criteria for an intramedullary implant, easy to place and effective for generating primary and secondary stability of the osteosynthesis or arthrodesis focus thanks to its stiffness and its compression component.

Invention

SUMMARY OF THE INVENTION

The inventive implant is characterized in that it comprises two bone anchoring zones on either side of a stiff stability zone, withstanding shear forces, these two anchoring zones having a possibility of high deformation at their base (in particular by elasticity) and a design such that they can adopt a closed position (in particular thanks to a suitable clamp closed at their base) for easy introduction into a calibrated centromedullary hole (prepared with an appropriate instrument), and in that owing to this particular configuration, they offer in the bone site the possibility of obtaining the final impaction without a distraction effect on the bone and sufficient expansion to ensure proper fixation in the bone.

The anchoring zones can be deformed at their base by elasticity, superelasticity or shape memory and typically consist of branches or legs, optionally connected (olive or rugby ball shape). In the open shape, these branches have an outward positive angle at their base and are curved inwardly toward their tips, whereas when the shape is closed, the angle of the base is reversed, that is negative or turned inwardly, thereby obtaining the width at the tips (impaction side) that is smaller than their base, in order to avoid impaction in the bone and blocking of the penetration of the implant.

The invention has a particularly advantageous application, which cannot however be considered as limiting, for the preparation of arthrodeses in the phalanges of the fingers and toes, especially for the proximal and distal interphalangeal joints in the hand and foot.

The device is implantable via the dorsal path (or optionally lateral or palmar/plantar), but without pulpar approach, thereby minimizing the risks of infection and improving the patient's comfort.

To take account of the anatomical features, the anchoring zones are connected to the median zone serving for strength (in particular shear) at the osteosynthesis focus by more or less long connecting zones, and the central zone may have a bend to adapt to the characteristics of the desired arthrodesis.

The material constituting the implant of the invention must allow a certain minimal opening of the anchoring zones once the implant is in the body. It may therefore be made from any sufficiently elastic implantable material such as stainless steel, titanium, a bioresorbable material such as polylactide acid PLLA.

Preferably, the implant of the invention is prepared from a shape memory material used for its property of superelasticity (or elasticity associated with the transformation of the austenite martensite phase under stress) which has the widest known elasticity range (up to 8% in elastic elongation equivalent in traction for an implant of Nitinol, a nickel-titanium alloy comprising about 55.5 to 56% by weight of nickel, the remainder being titanium).

It is also possible to use a material having a thermal shape memory around 37° C.

BRIEF DESCRIPTION OF THE DRAWING

The invention is described in greater detail below in conjunction with the appended drawings in which:

FIG. 1 shows an exemplary implant of the invention in its full open position in 3 dimensions,

FIG. 2 shows the same example in its closed introduction position in its main plane,

FIG. 3 shows an exemplary implant of the invention in its full open position, in its main plane,

FIG. 4 shows an example of a bent implant according to the invention in its full open position,

FIG. 5 (5 a to 5 f) shows the implantation sequence: closed, half introduced still stressed, fully introduced on one side (free in the bone), and the same sequence on the other side.

SPECIFIC DESCRIPTION

The implant is in the form of 2 anchoring zones A1 and A2 connected by a central zone C (FIG. 1) and optionally intermediate connecting zones such that in the closed position, the shape is substantially inscribed in a very elongated rectangle (FIG. 2), and in the open shape, corresponds to a wider X-shape due to the spreading of the anchoring zones A1 and A2 (FIG. 3).

The anchoring zones A1 and A2 each have two legs P1 and P2 having lengths L1 and L2 (FIG. 3).

The cross-section of the implant is adapted to the implantation sites, but preferably flat in order to have good mechanical strength and reduced size (typically the thickness e is about 1 to 2 mm) (FIG. 1).

FIG. 2 shows the closed position with the various widths of the implant: Lab is the width of the central zone C, L1 ab and L2 ab are the widths at the base of the anchoring zones A1 and A2. These 3 widths may be equal or slightly different to adapt to the bone site. Typically, the widths are about 2 to 5 times the thickness (or 2 to 10 mm). These dimensions are adapted to the various dimensions of the hand and foot but are not limiting because they depend on the bone site of the operated patient.

The anchoring zones A1 and A2 are suitable for separation by elastic effect or by shape memory effect at their base, so that the maximum width in the open position at the tips La1 and La2 (FIG. 3) is at least equal to the width of the base of the same anchoring zone in the closed position plus 50% minimum, or plus a minimum of 1.5 mm. This means that La1>L1 ab+50% or La1>L1 ab+1.5 mm and that La2>L2 ab+50% or La2>L2 ab+1.5 mm. This opening criterion is necessary to have sufficient fixation in the bone.

As shown in FIG. 3, the legs P1 (( ), (]] and P2 are substantially straight at their base (on about ⅓ to half of their length) and are then rounded inwardly at their tips (on about ⅓ to half of their length). In the open position, the straight inner portions of the legs P1 and P2 make positive outward angles a1 and a2 with the longitudinal implant axis A (FIG. 3), whereas in the closed position, these angles become inward negative angles b1 and b2 (FIG. 2). The upper or outer portions (toward the tip) of the legs P1 and P2 virtually undergoes no particular deformation between the two open and closed shapes.

This particular geometric arrangement ensures that in the closed position, the legs virtually touch at the tips (FIG. 2), and that the widths at the tips in the closed position La1 f and La2 f are lower than the widths at the respective bases L1 ab and L2 ab, thereby allowing easy introduction without distraction of the distal bone fragment and also obtaining the opened/closed movement by a local deformation at the base of the legs, that is by leaving the distal zone free for introducing this zone into the bone.

In order to obtain both easy introduction and sufficient opening movement, the angles a1 (( ), (]] and a2 are preferably between +5° and +25° and the angles b1 (( ), (]] and b2 between 0° and −15°.

Preferably, the widths of the tips of the anchoring zones in the closed position La1 f and La2 f are lower than the widths of the bases of these zones L1 ab and L2 ab, minus 20%: La1 f<L1 ab−20% and La2 f<L2 ab−20%.

The legs or anchoring zones are thus “articulated” at their base, and can therefore be secured in the closed position on a support or even better a clamp, positioned at an appropriate location defined in particular in the case of an elastic material (for a shape memory material, this is not absolutely necessary since the shape does not change as long as the activation temperature is not reached), this clamp not covering more than half of the length of the legs, thereby allowing introduction of at least half of the implant into its recess.

The inside tangents at the tip of the legs P1 and P2 in the open position make angles β1 and β2 with the longitudinal axis A of the implant close to 0°, in order to have a good bone contact area along the whole lengths of the legs in the open position and to prevent the bone from being touched by the tips alone (FIG. 3).

In the implant site, at body temperature, the implant can still be in the closed position, or parallel or with semiopen legs so that the force exerted by opening of the legs is transmitted to the bone and ensures proper fixation.

This “olive” arrangement of the legs, associated with an “articulation” of the base and associated with a minimal introduction of half of their length allows completion of the insertion, once the clamp has been removed.

In order to guarantee satisfactory operation, the elasticity or memory of the piece must allow a transition from the closed shape (typically width 2 to 4 mm according to the size of the site) to an open shape with a significant movement (+1.5 to +3 mm approximately).

Similarly, the force of expansion of the legs (or swelling of the olive) must be significant: typically 1 to 3 kg for an arthrodesis of the tips (force measured at 37° C. in the blocked introduction position), without being excessive: it is important for the legs to avoid opening completely and for the bone to resist so as to have a real holding force.

The legs P1 (( ), (]] and P2 or fins may have a rough surface or even better notches D (FIG. 3) on their outer surfaces intended to be press into the spongy bone and form a good anchorage. The typical depth of these notches HI (( ), (]] and H2 is about 0.5 mm. The opening of the legs must be at least 1.5 times this depth in order to ensure good engagement of the notches in the bone or 1.5 mm.

The legs P1 (( ), (]] and P2 may also have a surface covered with an osseointegration coating such as hydroxyapatite (HAP) intended to facilitate the anchorage.

To facilitate introduction into the bone, the tips of the legs P1 and P2 are beveled with an inward angle to the longitudinal axis A of the implant W1 and W2 (FIG. 3). This angle is typically between −20° and −40°.

By tests on fresh cadavers and experience, an optimal level of the force was determined with a minimum allowing anchorage of the notches in the spongy bone and a maximum force to be certain to avoid damaging the implantation site.

After tests and experience, an ideal zone was found with a maximum 20% of the elastic limit of the bone measured in a blocked closed shape at 37° C., which, considering the dimensions of the implant, gives rise to maximum values of about 3 kg, and the need for a rapid lowering as soon as the anchorage is obtained, or a force divided by 2 in the semi-open position (a force of 0.5 to 1.5 kg allows good holding). In fact, if the opening force is higher than about 3 kg, introduction into the bone becomes much more difficult, or even impossible above 4 kg. Finally, in order to guarantee a damage-free site, it is necessary for the force to become negligible for a virtually complete opening. These values are indicative and depend on the arthrodesis site and the bone quality.

In one version of the invention, the notches D1 and D2 on the outside of the legs P1 and P2 allow the positioning of a clamp and introduction at the base of the legs P1 (( ), (]] and P2 (FIG. 3). These notches are symmetrical by pairs of legs and their spacing d is the same on the legs P1 and on the legs P2.

The central zone C must have a minimum length Lc equal to the length d between the notches D1 and D2 so that even in case of movement of the implant during final impaction, this zone C remains in the arthrodesis focus and performs its resistance is function.

In one version of the invention, an orifice Or is provided in this central zone for positioning a holding pin to prevent migration of the implant at the time of final impaction.

As shown in FIG. 4, this central zone may be bent at an angle Ag defined between the 2 main planes formed by the legs P1 on the one hand and P2 on the other hand to adapt to the surgical requirements for adjusting the position of the arthrodesis. In most cases, the angle Ag is fixed between 0° (typically flat position for an index) and 30° (typically for a little finger).

As an example, an operating technique of implantation of the inventive device for the case of an elastic or superelastic implant is described as follows as shown in FIG. 5:

-   -   Approach by dorsal path     -   Resection of cartilages and osteophytes     -   Centromedullary perforation using an appropriate instrument to         make a calibrated rectangular hole having a width of         substantially L1 ab or L2 ab and thickness of substantially e         (by a suitable rasp)     -   Closure of the clamp side P1 (FIG. 5 a)     -   Implant introduction side P1 to minimum half (FIG. 5 b)     -   Clamp removal     -   Complete introduction side P1 (FIG. 5 c)     -   Closure of the clamp side P2 (FIG. 5 d)     -   Placement of the bone side P2 on the implant side P2 to about         half (FIG. 5 e)     -   Removal of the clamp     -   Manual impaction of the bone side P2 on the bone P1 (FIG. 5 f)

DETAILED DESCRIPTION OF THE FEATURES OF THE INVENTION AND EXEMPLARY EMBODIMENTS

In a particular embodiment, intended for a distal interphalangeal arthrodesis (hand), the implant is prepared from a superelastic Nitinol alloy (nickel-titanium in the weight proportion 55.8% nickel and 44.2% titanium).

The cross-section of the central zone C is Lab×e=2.8×1.2 mm and the legs are asymmetrical to adapt better to the shapes of the bone, minimize the implanted metal section and allow sufficient expansion for good anchorage. The length of the legs is L2=6.5 mm distal side P2 and L1=9 mm proximal side P1. The length of the central zone C is 3 mm, allowing a slight offset during closure, without affecting the shear strength. To adapt to the surgeon's choice, this central zone may be bent (typically flat or 15° or 25°).

In the closed position, the width of the proximal base L1 ab is 3.8 mm and of the distal base L2 ab is 3.0 mm. The opening of the legs P1 and P2 is 2.5 mm or 2.2 mm, that is La1 is 6.3 mm and La2 is 5.2 mm. In the open position the angle at the base of the legs is a1=10° and a2=22°. The straight portion is about 45% of the total length. The curvature of the distal tip of the legs is calculated so that the angle of the tangent at the tip is β1=−5° and β2=3°. In the closed position, the angle at the base of the legs is b1=−4°, b2=−2°. And the width at tip is La1 f=2.5 mm and La2 f=2.1 mm.

In one embodiment of the invention, the 0.5 mm deep notches are distributed on the legs (1 notch at approximately 0.8 mm spacings).

The angle of incidence of the tip of the legs (including notches) is w1=33° and w2=24°, allowing easy introduction without the distraction effect between the two bone pieces to be osteosynthesized.

The rounded design of the anchoring zones serves to obtain a maximized contact area over the entire length in the open shape, with an impaction effect in the spongy bone, and hence a spongy packing effect.

In another example, more appropriate for arthrodesis of the thumb, the dimensions are rather the following:

Closed widths: L1 ab=6.5 mm, L2 ab=5 mm, with an opening of 3 to 4 mm approximately to obtain: La1=11 mm and La2=8 mm and L1=13 mm and L2=9 mm. 

1. An intramedullary osteosynthesis and arthrodesis device for hand or foot bones and formed unitarily with a rigid central zone from opposite ends of which extend anchor zones each formed by a pair of legs extending symmetrically of a longitudinal axis generally bisecting the central zone, the legs each having a base portion fixed to the central zone and a tip forming the respective end, the end of one of the legs of a pair being independent of the other leg of the pair, the legs each further being deformable between a closed position for insertion of each of the pairs of legs into a respective bone and an open position for internally gripping the respective bone, the legs of each pair in the open position diverging away from the central zone and in the closed position converging away from the central zone so as to be more closely spaced at their tips than at their base portions, the base portions of each pair of legs in the closed position being angled inwardly towards one another, wherein an outer surface of each leg is curved at the tip and, in the open position, the outer surface of each leg is adapted to form an anchorage within the respective bones.
 2. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein the legs each have a predetermined length measured parallel to the axis and the respective base portions and tips each occupy between one-third and one-half of the length of the respective leg.
 3. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein the device is made of an elastic or superelastic memory material.
 4. The intramedullary osteosynthesis and arthrodesis device defined in claim 3 wherein the memory material is thermally activatable.
 5. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein in the open position the base portions of the legs of each pair form at the outwardly open angle of between 5′ and 25′ and the inside tangent of the tip of said legs make an angle with longitudinal axis close to 0°.
 6. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein in the closed position the base portions of the legs of each pair form an outwardly open angle of between 0° and −15° such that an overall width measured transversely of the axis of the device at the tips is smaller than at the base portions.
 7. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein in the open position the tips of the legs of each pair define a transverse width measured transversely of the axis that is greater by 50% or 1.5 mm than a transverse width of the legs of each pair where the respective base portions join the central zone.
 8. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein, in the closed position, the width of the tips of the anchor zones of each pair is smaller than a transverse width of a respective base portions by 20%.
 9. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein the tips are beveled.
 10. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein the tips of the legs are formed with outwardly directed notches or are roughened.
 11. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein the outer surfaces of the legs are formed with outwardly directed notches set at a sufficiently wide spacing at the base portions to allow gripping by a clamp.
 12. The intramedullary osteosynthesis and arthrodesis device defined in claim 11 wherein the central zone has a length measured parallel to the axis generally equal to the wide notch spacing.
 13. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein the legs and central zone are generally flat and the central zone is formed with a bend such that the anchor zones extend at an angle Ag comprised between 0° and 30°.
 14. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein the device is made of such a material that the force of the expansion of the legs in the blocked introduction position is between 1 kg and 3 kg.
 15. The intramedullary osteosynthesis and arthrodesis device defined in claim 1 wherein each leg further comprises a length, the length is adapted to obtain a contact area along the outer surface over the length with the respective bone to form the anchorage.
 16. An intramedullary osteosynthesis and arthrodesis device for hand or foot bones and formed unitarily with a rigid central zone from opposite ends of which extend anchor zones each formed by a pair of legs extending symmetrically of a longitudinal axis generally bisecting the central zone, the legs each having a base portion fixed to the central zone and a tip forming the respective end, the legs each further being deformable between a closed position, where the device adopts an H-shape, for insertion of each of the pairs of legs into a respective bone and an open position, where the device adopts an X-shape, for internally gripping the respective bone, the base portions of each pair of legs in the open position diverging away from one another and in the closed position converging towards one another such that the legs of each pair are more closely spaced at their tips than at their base portions when in the closed position wherein an outer surface of each leg is curved at the tip and, in the open position, the outer surface of each leg is adapted to form an anchorage within the respective bones.
 17. The intramedullary osteosynthesis and arthrodesis device defined in claim 16 wherein the legs each have a predetermined length measured parallel to the axis and the respective base portions and tips each occupy between one-third and one-half of the length of the respective leg.
 18. The intramedullary osteosynthesis and arthrodesis device defined in claim 16 wherein the device is made of an elastic or superelastic memory material.
 19. The intramedullary osteosynthesis and arthrodesis device defined in claim 18 wherein the memory material is thermally activatable.
 20. The intramedullary osteosynthesis and arthrodesis device defined in claim 16, wherein in the open position the base portions of the legs of each pair form at the outwardly open angle of between 5° and 25° and the inside tangent of the tip of said legs make an angle with the longitudinal axis close to 0°, and wherein in the closed position the base portions of the legs of each pair form an outwardly open angle of between 0° and −15° such that an overall width measured transversely of the axis of the device at the tips is smaller than at the base portions. 